Sumitomo Wearplate K400, K450 and K500

Product:Sumitomo Wearplate
Grade:K400, K450 and K500
Kategori:Wear Resistant Plate
Negara Asal:Jepang

Description
Sumitomo Wearplate 400, 450 and 500 is a through hardened abrasion resistant steel with a typical hardness of 415 BHN, 490 BHN, and 510 BHN. These steels are the most widely used of the wear resistant grades. They exhibit an excellent combination of high resistance to impact, workability, Weldability and resistance to abrasion. It has about 5 times the abrasion resistance of common steel plate and contribute to prolonging the service life of mechanical parts.

Availability Klik Disini


Chemical Composition %

CSiMnPSB
0.210.701.600.0250.010.003

Mechanical Properties
Brinell Hardness: 360-440
Heat Treatment: Quenched & Tempered
Yield Point min MPa: 1156 MPa
Tensile Strength MPa: 1325 MPa
Elongation: 25%

Cutting
Cutting is possible with oxy-propane, oxy-acetylene, plasma, laser and water.
Stack cutting should be avoided.
After gas cutting, the steel plate should not be sprayed or cooled with water.
Tungsten Carbide tools are recommended with close attention to cutting speeds and feeds.

Machining
Machining speeds are 50-70% of plain carbon steel. Constant feed and lubrication should be maintained.

Forming
Cold forming can be carried out using the following guidelines

Welding
Welding can be carried out by manual metal arc, submerged arc or gas metal arc welding. Because the properties of Sumihard 400 results from quenching and tempering, to obtain optimum results the following recommendations should be served when welding.
  • Electrodes and fluxes should be of the low hydrogen type, baked and stored strictly in accordance with the manufacturers recommendations.
  • It is recommended that Sumihard 400 be preheated to a suitable temperature to eliminate the risk of cold cracking in the weld area.
  • The selection of preheat temperatures are dependant upon the plate thickness, geometry and other associated factors. The minimum preheat temperatures for optimum results are set.
Applications
Dump Truck Liners, Ripper Tynes, Bucket Wear Liners, Cutting Edges, Mining Liner Plates, Agricultural Machinery, Chute Liners, Crusher Liner Plates, Hoppers Liners, Shredder Blades, Mixing Blades, Feeders, Crushers, sievers, feeders, measuring pockets, skips, cutting edges, conveyors, buckets, knives, gears, sprockets, dumptrucks, loaders, industrial trucks, lorries, bulldozers, excavators, slurry pipe systems, screw conveyors


Steel Plate Product:

Produk Terkait:

Tags:
  • #toko besi terdekat, Jual plat Hardox,jual plat abrex 500,plate 253MA stainless, harga Plat 3cr12,plat Everhard C-400,XAR wear plate,quard plate, Jual plate raex 400, Creusabro 8000, plate weldox, Harga Baja, #jual stainless steel 304/L, as stainless 316, plat stainless 310s, sf003 steel plate,Jual plat A283 Gr.C bekasi,harga plat A516 Gr.70, stainless 410s Durinox,Jual Steel Pipe, distributor baja KS, GRP, dual plate,jual steel holo, harga steel roundbar terbaru, ASTM A572 grade 50, daftar harga stainless 2023,jual besi kotak,Aluminium plate 7075, material baja preharden,material stavax, jual vcn steel, Harga besi holo,inp,wf, unp,cnp,,H-beam,besi beton,Steel AISI 4340, harga Plate Boiler A387 Gr.22,jual valve dan flange,plat Kapal SS400,A36, BKI plate,SPCC SD, SPHC,Plat S355JR steel, harga plate sm490 YA, ABS, abrasion,Marine plate, plate Corten, Sumihard,Offshore plates,plat bisalloy,